Method to improve film property

ABSTRACT

The present invention relates to offer a method to improve the property of films comprising a release film and a protective film. After separating from the release film, the protective film is bonded with TAC (Triacetyl Cellulose) film and then processed by relative coating, such as anti-reflecting coating, anti-glaring coating and surface hardening treatment, drying in an oven and separated the protective film from the TAC film. The present invention prevents the material consuming, which resulted from crack, snap and bend of the film in the process; and furthermore, practice costs is not too much and no additional expensive apparatus or treatment is necessary for a simplified procedure of the method.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method to improve properties of a film composing of a release film and a protective film. The protective film is bonded with a TAC (Triacetyl Cellulose) film after separating from the release film. The pasted TAC film is processed by relative coating, such as anti-reflecting coating, anti-glaring coating and surface hardening treatment, dried in an oven and the protective film is separated from the TAC film.

2. Description of the Prior Art

As the science being developed day-by-day and advanced greatly, the products for high technologies are focused on the principles of small volume, lightweight for the marketing. It causes that the procedures for manufacturing may be considered more than before. For example, a film is very fragile to be cracked or bended due to the thin thickness thereof, hence, the cost of raw materials is over consumed. In the field, there is no solution to figure out above issue, and a prior art for another field is provided hereinafter for discussion.

A Taiwan patent, numbered 524748, teaches a method for posting a film up, especially to the method of posting film up is described as following: a scrolled film by composition of a base film, a bottom film and a surface film is stripped firstly, that is, the surface film is removed, and the scrolled film is moved while in arrangement of a film body facing to a side of the base film, the film body and the base film are then gone to rolling so as to that the film body being posted upon the base film, wherein the features are: to remove portions between the base film and the film body without sticking together and portions of the film body stuck together by rolling, thus after the portions being exposed, the film body being stuck on a surface of the base film by way of aforesaid rolling.

Another Taiwan patent, numbered 546728, is related to a sticky film for protecting a wafer surface of semiconductor, and the features are: a single surface of a base film being mounted at least one middle layer and an agglutinant layer, and a min. value (G′min) range of a storing flexibility rate (G′) of the agglutinant layer (B) in the temperature range of 50 to 100° C. is between 0.07 to 5 Mpa, the storing flexibility rate for the middle layer (C) at 50° C. is above 0.001 Mpa, but not approaching to 0.07 Mpa, a total thickness (μm) of the agglutinant layer's thickness (tb) and the middle layer's thickness (tc) meets the following equation: tc≧3 tb.

The third Taiwan patent, numbered 498318, discloses a method for manufacturing a protecting film of a recording information disk, which means to manufacture a magnetic film for recording information on a surface of a substrate, and continuously a protecting film being made on the magnetic film. The features for the patent are: a manufacturing temperature for the protecting film is higher than a manufacturing temperature for the magnetic film, further, after the magnetic film is made, the substrate is then heated so as to approach the temperature for making the protecting film.

The fourth Taiwan patent, numbered 553828, is a method for sticking a film. That is to adopt a pressing roller to roll over a film on a substrate so as to that the film being stuck on the substrate. The feature is that the pressing roller is capable of maintaining the film in a certain status, that is, an outer circumference surface of the pressing roller maintains a front portion of the film, the front portion willing to be stuck; continuously the pressing roller is rotated to deliver the film to the substrate so as to that the front portion exactly meeting with a position for starting sticking, the film is then adhered on the substrate; a rear portion of the film willing to be stuck may be kept by the outer circumference surface as well. Therefore, as a conclusion, the pressing roller is the role to post from the front portion to the rear portion of the film on the substrate.

Above prior arts may cooperate with expensive equipment or require pre-processing, it is obvious that the cost cannot be down; further that, complicate procedures certainly increase the difficulty and the fault possibility.

SUMMARY OF THE INVENTION

The present invention relates to a method to improve properties of film. The first objective of the present invention is to prevent the material consuming, which resulted from cracks, snaps and bends of the film in the process.

The present invention relates to a method to improve properties of film. The second objective of the present invention is to offer a method that practice costs is not too much and no additional expensive apparatus or treatment is necessary for a simplified procedure of the method.

The present invention relates to a method to improve properties of a film composing of a release film and a protective film. The protective film is bonded with a TAC (Triacetyl Cellulose) film after separating from the release film. The bonded TAC film is processed by relative coating, such as anti-reflecting coating, anti-glaring coating and surface hardening treatment, dried in an oven and the protective film is separated from the TAC film.

Other and further features, advantages and benefits of the invention will become apparent in the following description taken in conjunction with the following drawings. It is to be understood that the foregoing general description and following detailed description are exemplary and explanatory but are not to be restrictive of the invention. The accompanying drawings are incorporated in and constitute a part of this application and, together with the description, serve to explain the principles of the invention in general terms. Like numerals refer to like parts throughout the disclosure.

BRIEF DESCRIPTION OF THE DRAWINGS

The objects, spirits and advantages of the preferred embodiments of the present invention will be readily understood by the accompanying drawings and detailed descriptions, wherein:

FIG. 1 is a process diagram of the present invention.

FIG. 2 is a bonding process for a TAC (Triacetyl Cellulose) film and a protective film of the present invention.

FIG. 3 is a coating process for anti-reflecting, anti-glaring and surface hardening of the present invention.

FIG. 4 is a separating process of the anti-reflecting TAC film from the protective film.

DETAILED DESCRIPTION OF THE PREFFERED EMBODIMENT

With reference to FIG. 1, which relates to a process diagram of the present invention. The process broadly comprises three stages: film bonding (steps 111˜116), coating (steps 117˜122) and film separating (steps 123˜126). A method of the present invention is described as following.

With reference to FIG. 2, which presents a bonding process (steps 111˜116 in FIG. 1) for a TAC (Triacetyl Cellulose) film and a protective film of the present invention. At first, a PE (polyethylene) film 201 is used. The PE film 201 comprises a release film and a protective film having a gluey face on it (step 111 in FIG. 1). In a practice field, however, a PET (polyenthylene Terephthalate) film is also used instead of the PE film. The PE film 201 twined on a roller (step 112 in FIG. 1) is rolled out (step 113 in FIG. 1) to an oven 205 by assistance of rollers 202, 203 and 204. The oven 205 is not operated at this time.

The PE film 201 coming over the oven 205 is assisted by rollers 206, 207 and 208 to separate a release film from the protective film. When the film 201 steps in the roller 209, the release film having no gluey face is separated from the protective film (step 114 in FIG. 1) and gathered in a release film roller 210. Parameters including of an appropriate tension and rolling rates of the roller are relative to separating the release film from the protective film.

After separating from the release film, the protective film is bonded with a TAC film 213 by functioning of rollers 211 and 212 (step 115 in FIG. 1). A variety of parameters have to be considered in this step, including of the tension, the rolling rates, bonding speeds and viscosity of glues on the protective film. Then, the bonded film 214 is rolled-in (step 116 in FIG. 1) and the bonding process is finished (steps 111˜116).

With reference to FIG. 3, which presents a coating process (steps 117˜122 in FIG. 1) for anti-reflecting, anti-glaring and surface hardening. The bonded film 301 composing of the protective film and the TAC film is rolled-out (step 117 in FIG. 1) by a roller 302 and processed by relative coating, such as anti-reflecting coating, anti-glaring coating and surface hardening treatment (step 118 in FIG. 2). Parameters including of the tension, coater speeds and drying temperatures have to be considered in the coating process. A variety of coating types and TAC film thickness are adopted in the present invention. An oven 305 is switching on (step 119 in FIG. 1) after the film finishes coating. The TAC film 301 is dried in the oven 305 by functioning of rollers 303 and 304 (step 120 in FIG. 1) and then rolled-in by rollers 306, 307 and 308 to relative coating, such as anti-reflecting coating, anti-glaring coating and surface hardening treatment (step 121 in FIG. 1) for the TAC film 309. The oven 305 is switching off after rolling-in (step 122 in FIG. 2) and the coating process is finished (steps 117˜122).

With reference to FIG. 4, which presents a separating process of the anti-reflecting TAC film from the protective film (steps 123˜126 in FIG. 1). The TAC film 401 processed by relative coating, such as anti-reflecting coating, anti-glaring coating and surface hardening treatment is rolled-out (step 123 in FIG. 1) and then rolled into a oven 405 by functioning of rollers 402, 403 and 404. The oven 405 is switching off at this moment. By functioning of rollers 406, 407 and 408, the TAC film 401 is rolled for the separating process.

While the TAC film 401 stepping into a roller 409 and a roller 410, the protective film is separated from the TAC film (step 124 in FIG. 1) and gathered in a protective film roller 411. Parameters including of an appropriate tension and rolling rates of the roller are relative to separating the protective film from the TAC film. The separated TAC film is gathered in a TAC film roller 412 (step 125 in FIG. 1) and the separating process is finished (steps 123˜126).

The present invention prevents the material consuming, which resulted from crack, snap and bend of the film in the process; and furthermore, practice costs is not too much and no additional expensive apparatus or treatment is necessary for a simplified procedure of the method.

Although this invention has been disclosed and illustrated with reference to particular embodiments, the principles involved are susceptible for use in numerous other embodiments that will be apparent to persons skilled in the art. This invention is, therefore, to be limited only as indicated by the scope of the appended claims. 

1. A method to improve properties of a film composing of a release film and a protective film, the method comprising: (1) separating the release film from the protective film; (2) bonding a TAC (Triacetyl Cellulose) film with the protective film; (3) processing the bonded TAC film by relative coating and then drying in an oven; (4) separating the protective film from the TAC film; (5) the method finishing.
 2. The method to improve properties of a film according to claim 1, wherein the film is a PE (Polyethylene) film.
 3. The method to improve properties of a film according to claim 1, wherein the film is a PET (Polyethylene Terephthalate) film.
 4. The method to improve properties of a film according to claim 1, wherein (1) comprises the following steps: (1A) preparing each of a PE film and a PET film; (1B) rolling the PE film on a roller; (1C) rolling out the PE film on the roller; (1D) separating the PE film into a protective film and a release film;
 5. The method to improve properties of a film according to claim 1, wherein (2) comprises the following steps: (2A) bonding the TAC film with the protective film; (2B) rolling-in the bonded TAC film;
 6. The method to improve properties of a film according to claim 1, wherein (3) comprises the following steps: (3A) rolling out the bonded TAC film; (3B) processing the bonded TAC film by relative coating; (3C) switching on the oven; (3D) drying the bonded TAC film after coating; (3E) rolling-in the bonded TAC film after drying; (3F) switching off the oven; (3G) rolling-in the dried TAC film;
 7. The method to improve properties of a film according to claim 1, wherein (4) comprises the following steps: (4A) rolling out the dried TAC film; (4B) separating the protective film from the TAC film; (4C) rolling in the TAC film after separating;
 8. The method to improve properties of a film according to claim 6, wherein the relative coating in (3B) comprises the followings: anti-reflective coating, anti-glaring coating and surface hardening treatment. 